ISSUED : January 1997
NANCAR®
6004
is a medium low
acrylonitrile butadiene copolymer. It is polymerized at low temperature and
contains sufficient antioxidant for normal aging conditions.
NANCAR®
6004
is recommended for use in applications requiring improved low temperature
properties, oil resistance, water resistance and anti-metal corrosion. It
provides good processability and low mold staining properties.
NANCAR®
6004
is designed for products
requiring exposure to extremely low temperatures while maintaining good oil
resistance, for instance, aircraft equipment parts and other industrial spare
parts.
|
POLYMER PROPERTIES
|
TYPICAL
VALUE
|
TEST
METHOD
|
|
Bound
acrylonitrile, %
|
19
|
NANTEX
E-001
|
|
Mooney
viscosity, ML1+4 @100oC
|
63
|
ASTM
D-1646
|
|
Heat
loss, %
|
0.5
|
ASTM
D-1416
|
|
Specific
gravity
|
0.94
|
|
Stabilizer
|
Non-staining
|
|
TEST RECIPE:ASTM
D-3187
|
PARTS
|
|
NANCAR®
6004
|
100.00
|
|
|
Zinc
Oxide, NBS 370
|
3.00
|
|
|
Sulfur,
2% MgCO3 coated
|
1.50
|
|
|
Stearic
Acid, NBS 372
|
1.00
|
|
|
HAF
Black IRB#6
|
40.00
|
|
|
TBBS,
NBS 384
|
0.70
|
|
|
Total
|
146.20
|
|
|
COMPOUND PROPERTIES,
UNCURED STOCK
|
TYPICAL
VALUE
|
TEST
METHOD
|
|
Compound
Mooney, ML1+4 @100oC
|
84
|
ASTM D-1646 |
|
Mooney
scorch, large rotor, 125oC
|
|
ASTM D-1646
|
|
Minimum
viscosity, Vm
|
60
|
|
Minutes
to 5 points rise, t5
|
29.5
|
|
Minutes
to 35 points rise, t35
|
37.5
|
|
COMPOUND PROPERTIES,
CURED @150oC
|
MINUTES
|
TYPICAL
VALUE
|
TEST
METHOD
|
|
Tensile
Strength, Kg/cm2
|
40
|
205
|
ASTM D-412 |
|
Elongation,
%
|
40
|
520
|
ASTM D-412 |
|
Modulus
at 300% Elongation, Kg/cm2
|
20
|
90
|
ASTM D-412
|
|
40
|
93
|
|
60
|
98
|
|
Hardness,
Durometer A, points
|
40
|
64
|
ASTM D-2240 |
|
Compression
Set, 100oCx70hrs, %
|
60
|
60
|
ASTM D-395 |
|
AGING PROPERTIES,
CURED @150oCx40 MINUTES
|
TYPICAL
VALUE
|
TEST
METHOD
|
|
ASTM
#1 Oil Immersion, @100oCx70hrs
|
|
ASTM
D-471
|
|
Tensile
strength change, %
|
+1
|
|
Elongation
change, %
|
-14
|
|
Hardness
change, points
|
-5
|
|
Volume
change, %
|
+6.5
|
|
|
|
|
|
ASTM
#3 Oil Immersion, @100oCx70hrs
|
|
ASTM
D-471
|
|
Tensile
strength change, %
|
-58
|
|
Elongation
change, %
|
-36
|
|
Hardness
change, points
|
-24
|
|
Volume
change, %
|
+59.5
|
|
|
|
|
|
Test
Tube Heat Aging, @100oCx70hrs
|
|
ASTM
D-865
|
|
Tensile
strength change, %
|
+3
|
|
Elongation
change, %
|
-25
|
|
Hardness
change, points
|
+4
|
NANCAR®
is the registered trade mark of nitrile rubber manufactured by NANTEX
INDUSTRY CO., LTD.
|